BAg-5 Type(Ag-Cu-Zn 3 Elements)

BAg-4 Type(Ag-Cu-Zn-Ni 4 Elements)

BAg-7 Type(Ag-Cu-Zn-Sn 4 Elements)

5 Elements(Ag-Cu-Zn-In-Mn)

It has been widely used in each industry as well electronics that BAg-1, BAg-1A,
BAg-2 and BAg-3 out of 10 types internationally standardized Silver Filler Metals,
but it contains much amount of cadmium (Cd) of 15~20%.
Therefore our reseachers developed Cd-Free Silver Filler Metal more safe and
excellent than existing one to solve safety problems caused by heavy metal
cadmium pollution.

Alloy		Composition(%)						Melting Point(℃)
Alloy		Ag	Cu	Zn	Sn	In	other	Solidus	Liquidus
50% Ag	BAG-7	56	22	17	5			620	650
	BAG-6	50	34	16				690	775
	HS-451	45	25	25		5		650	690
	HS-452	45	26	21		5	Ni3	665	685
	HS-454	45	22	25		5	Ni2 Mn1	635	700
	HS-501	50	30	15	5			665	690
45% Ag	BAG-5	45	30	25		5		675	745
	HS-401	40	30	25				635	715
	HS-455	45	25	30				670	700
40% Ag	BAG-4	40	30	28			Ni2	670	780
	HS-23	40	30.5	29.5				621	732
	HS-34	40	40	20	2			697	795
	HS-402	40	30	28				640	700
	HS-403	40	30	29		1		662	717
35% Ag	HS-301	30	38	27		5		640	755
	HS-351	35	35	30				675	750
	HS-352	35	30	25	2		Mn8	690	720
	HS-353	35	30	30			Mn5	690	730
	HS-331	33	38	27	2			642	760
	HS-341	34	35	30		1		667	750
	HS-355	35	32	31	2			660	740
30% Ag	HS-302	30	37	32	1	1		670	760
	HS-25	30	38	32		1		695	766
	HS-291	29	39	31			Mn3 Sil	670	760
25% Ag	HS-251	25	43	32				760	785

specification		HS301	HS302	HS331
Composition		Ag : 30	Ag : 30	Ag : 33
		Cu : 38	Cu : 37	Cu : 38
		Zn : 27	Zn : 32	Zn : 27
		In : 5	Sn : 1	Sn : 2
Physical Properties	M. P.	640~755 ℃	690~760℃	642~760℃
	Brazing Temp.	755~880℃	760~890	760~880℃
	Specific Gravity	8.64	8.61	8.73
	Tensile Strength	40 kg/㎟	30 kg/㎟	35kg/㎟
	Elasticity	15%	12%	14
Applicable Metal		Cu, Cu alloy, Stainless Steel, Fe alloy
Color after Brazing		White color
Characteristics of Cd-Free filler		1) It is fee of Cd, replacing the fluidity of Cd with those of In, Sn to provide low melting point and rich flow (fluidity) and corrosion resistance. 2) As it has tendency not to be melted if heating slowly at the above-shown melting point range, it is recommended to heat quickly.